ASTM A519 specification covers for several grades of carbon and alloy steel mechanical tubing, either hot-finished or cold-finished.
An analysis of each heat of steel shall be made by the steel manufacturer to determine the percentages of the elements specified; if secondary melting processes are used, the heat analysis shall be obtained from one remelted ingot or the product of one remelted ingot of each primary melt.
The heat analysis shall conform to the requirements specified, except that where the heat identity has not been maintained or where the analysis is not sufficiently complete to permit conformance to be determined, the chemical composition determined from a product analysis made by the tubular manufacturer shall conform to the requirements specified for heat analysis. When requested in the order or contract, a report of such analyses shall be furnished to the purchaser.
When specified, steel prior to shipment should be greased to prevent rusting. If the order is not specified in the shipment oiled steel, coated with a layer of oil production should remain on the surface. If the order is not specified in oiled side response is required during transport rusty responsibility. Unless otherwise specified, the manufacturer can be arbitrary inner and outer surfaces of the pipe coated with anti-rust oil.
Grade | C | Mn | P | S | Si | Cr | Mo |
4118 | 0.18-0.23 | 0.70-0.90 | 0.035 | 0.040 | 0.15-0.35 | 0.40-0.60 | 0.08-0.15 |
0.28-0.33 | 0.40-0.60 | 0.035 | 0.040 | 0.15-0.35 | 0.80-1.10 | 0.15-0.25 | |
4135 | 0.33-0.38 | 0.70-0.90 | 0.035 | 0.040 | 0.15-0.35 | 0.80-1.10 | 0.15-0.25 |
4140 | 0.40-0.45 | 0.75-1.0 | 0.035 | 0.040 | 0.15-0.35 | 0.80-1.10 | 0.15-0.25 |
Grade | Tenslle strength(Mpa) | Yield strength(Mpa) | Elongation(%) | RB |
4118 | 685 | 885 | 12 | 197 |
785 | 930 | 12 | 229 | |
4135 | 835 | 980 | 12 | 229 |
4140 | 930 | 1080 | 12 | 217 |
Pipe Type | Pipe Sizes | Tolerances | |
Cold Drawn | OD | ≤48.3mm | ±0.40mm |
WT | ≥60.3mm | ±1%mm | |